Silicate erogba biriki je ti didoju refractory, eyi ti o withstands ogbara ti acid ati alkali slags, olomi, ati awọn miiran kemikali ipata. Silikoni carbide ni awọn ohun kikọ ti agbara giga, resistance anti-oxidation ti o dara, ati pe ko si iyipada ni iwọn otutu giga. Ninu gbogbo awọn ohun elo aise ti awọn biriki ti kii ṣe afẹfẹ, biriki carbon slilica jẹ ọrọ-aje julọ ati lilo pupọ julọ ni awọn aaye kan. eyiti o le ṣee lo ni awọn ile-iṣẹ oriṣiriṣi, gẹgẹbi ile-iṣẹ okuta, ile-iṣẹ gilasi, ile-iṣẹ irin, ile-iṣẹ titẹ, ati ile-iṣẹ ina. Yato si, Silica erogba biriki fun tita ni o ni Elo o tayọ išẹ lori koju gidigidi buburu ogbara ayika, gẹgẹ bi awọn ooru elekitiriki, ti o dara abrasive resistance, gbona mọnamọna resistance, lagbara sooro si acid ati alkali slag ogbara ati kekere ooru imugboroosi olùsọdipúpọ ati be be lo.
Awọn ohun elo aise silicate carbide block jẹ ohun alumọni carbide, nipa 72% -99%. Ohun alumọni carbide tun ni a npe ni moissanite, corundum iyanrin tabi iyanrin refractory. eyi ti a ṣe nipasẹ iyanrin quartz, epo epo koke tabi oda edu, ati awọn ege igi, ti a ṣe nipasẹ didan otutu otutu ni ileru resistance ina.
Biriki carbide silikoni jẹ iṣelọpọ lati inu ohun alumọni ohun alumọni, ohun elo aise ti a ṣepọ ni ileru ina mọnamọna iru resistance ni iwọn otutu ti o kọja 2500 ° C, nipasẹ ifa ti yanrin pẹlu erogba. Awọn biriki erogba silcate ni adaṣe igbona ni igba mẹwa ti awọn isọdọtun fireclay, ipata ti o dara ati resistance mọnamọna gbona, ati pe o le ṣẹda sinu awọn apẹrẹ eka. Biriki cabon Silica le koju ikọlu slag ati ogbara ina.
Silicon carbide refractory biriki le ti wa ni classified sinu amo iwe adehun ohun alumọni carbide biriki, Si3N4 bonded silikoni carbide biriki, Sialon bonded silikoni carbide biriki, β-SiC iwe adehun ohun alumọni carbide biriki, Si2ON2 bonded silikoni carbide biriki ati recrystal silikoni carbide biriki.
Silikoni Carbide biriki | |||||
Awọn nkan | Ẹyọ | SiO2 iwe adehun Silicon Carbide Bricks | Azokty-cornpounds iwe adehun Silicon Carbide Bricks | Mullite iwe adehun Silicon Carbide Bricks | |
Al2O3 | % | ~ | ~ | ≥10 | |
SiO2 | % | ≤8 | ~ | ~ | |
Fe2O3 | % | ≤1 | ≤0.6 | ≤1 | |
Sic | % | ≥90 | ≥80 | ≥85 | |
Porosity ti o han gbangba | % | ≤18 | ≤18 | ≤18 | |
Olopobobo iwuwo | g/cm3 | ≥2.56 | ≥2.60 | ≥2.56 | |
Tutu crushing Agbara | Mpa | ≥80 | ≥100 | ≥70 | |
Refractoriness labẹ Fifuye | ℃ | ≥1600 | ≥1620 | ≥1550 | |
Gbona mọnamọna Iduroṣinṣin (Akoko/850) | ℃ | ≥40 | ≥40 | ≥35 | |
Gbona Conductivity | w/m*k | ≥8 | ~ | ~ | |
Deede otutu atunse Agbara | Mpa | ≥25 | ≥30 | ≥25 | |
Agbara Lilọ Iwọn otutu giga1250 ℃ * 1h | Mpa | ≥20 | ≥25 | ≥20 | |
O pọju Service otutu | ℃ | 1400 | 1500 | 1400 |
Biriki carbide Silica ni ifarakanra gbona giga, resistance yiya ti o dara, resistance mọnamọna gbona ati resistance ipata. Nitorinaa brick carbon silica ni ọpọlọpọ ohun elo bi atẹle: