Ina iwuwo Clay idabobo biriki Apejuwe
Ina iwuwo Clay idabobo biriki ti wa ni ṣe ti ina amo grog bi awọn aise ohun elo ati ki ṣiṣu amo bi awọn abuda oluranlowo ki o si fifi o dara combustible tabi foomu oluranlowo nipasẹ tita ibọn. Awọn bulọọki idabobo amọ ti o han gbangba porosity jẹ giga nipa 40 ~ 85% ati iwuwo olopobobo ni isalẹ ju 1.5 g/cm3. Awọn biriki ina idabobo amọ ni a lo ni akọkọ bi awọn ohun elo idabobo ni kiln ile-iṣẹ lati dinku isonu ooru ti kiln, fi agbara pamọ ati mu didara ohun elo igbona.
Awọn ohun-ini ti Biriki Imudaniloju Amo iwuwo Ina
- Iwọn irin kekere ati awọn aimọ miiran,
- Refractoriness giga,
- Porosity giga, iwuwo iwọn kekere,
- Ipa idabobo ooru to dara ati agbara daradara,
- Iduroṣinṣin mọnamọna gbona gbona,
- Ipata ati ogbara resistance.
Ilana iṣelọpọ ti Biriki Imudaniloju Amo iwuwo Imọlẹ
Biriki Imudabo Amo iwuwo Imọlẹ jẹ iṣelọpọ lati inu amọ ina mimọ ti o ga ati dipọ, nipasẹ sisọ nipasẹ iwọn otutu giga. Awọn bulọọki idabobo amọ jẹ awọn biriki idabobo iye owo kekere pẹlu iṣẹ ṣiṣe giga. Awọn anfani akọkọ ti bulọọki idabobo amo jẹ isọdọtun giga labẹ ẹru, awọn iye iwọn ilawọn ila kekere, resistance mọnamọna gbona ti o dara ati agbara to lagbara lati koju ogbara. Eyi ti o jẹ ti awọn ohun elo ina ti oke ti agbegbe labẹ iwọn otutu giga ni ibamu si boṣewa orilẹ-ede ti o kẹhin, eyiti o ni iwuwo pupọ paapaa, agbara giga, adaṣe igbona kekere ati aimọ kekere.
Tiwqn ti Light iwuwo Clay idabobo biriki
Brick firebrick idabobo amo jẹ ọja argillaceous pẹlu nipa 30 ~ 40% akoonu Al2O3. eyiti o jẹ ti 50% amọ rirọ ati 50% chamotte lile ni ibamu si awọn granularity kan nilo lati dapọ ati ina ni 1300 ~ 1400 ℃ otutu otutu lẹhin mimu ati gbigbe. Amo idabobo ina biriki akọkọ ni erupe ile tiwqn pẹlu kaolinite (Al2O3 · 2SiO2 · 2H2O) ati 6 ~ 7% impurities (K, Na, Ca, Ti, Fe oxide).
Rongsheng Refractory Light iwuwo Clay idabobo biriki pato
| Awọn nkan | NG-0.6 | NG-0.8 | NG-1.0 | NG-1.3 | NG-1.5 | |
| O pọju Service otutu | 1200 | 1280 | 1300 | 1350 | 1400 | |
| Ìwúwo Olopobobo, g/cm3 | 0.6 | 0.8 | 1.0 | 1.3 | 1.5 | |
| Pàtàkì àìdára,% | 70 | 60 | 55 | 50 | 40 | |
| Agbara fifun tutu (Mpa) ≥ | 2.0 | 2.5 | 3.0 | 4.0 | 6.0 | |
| Iyipada Laini Atunṣe (%)℃×12h ≤ | 1300 ℃ -0.5 | 1350 ℃ -0.5 | 1350 ℃ -0.9 | 1350 ℃ -0.9 | 1350 ℃ -0.9 | |
| Imudara igbona W/(m·K) | 600 ℃ | 0.16 | 0.45 | 0.43 | 0.61 | 0.71 |
| 800 ℃ | 0.18 | 0.50 | 0.44 | 0.67 | 0.77 | |
| Al2O3 | 40 | 40 | 40 | 40 | 42 | |
| SiO2 | 1.5 | 1.5 | 1.5 | 2 | 2 | |
| Fe2O3 | 55 | 55 | 55 | 55 | 55 | |
Ohun elo ti Light iwuwo Clay idabobo biriki
Bulọọki idabobo amọ jẹ lilo nipataki fun ikan idabobo ti awọn ibi ti o gbona tabi atilẹyin awọn ipele idabobo ooru ti awọn ohun elo itusilẹ miiran. Awọn ohun elo ifasilẹ tabi awọn ohun elo idabobo ooru ti awọn ile-iṣẹ, gẹgẹbi, awọn ileru pyrolysis ethylene, awọn ileru tubular, awọn ileru ti n ṣatunṣe ti amonia sintetiki, awọn olupilẹṣẹ gaasi ati awọn kilns iwọn otutu giga, ati bẹbẹ lọ.